HARDBOLT ANCHOR BOLT – CARBON STEEL
DESCRIPTION |
RECOMMENDED
DRILL BIT |
TIGHTENING
WRENCH |
U.M. |
QUANTITY PER PACKAGE – PORTIONED (PIECE) |
QUANTITY PER PACKAGE – MASTER (PIECE) |
M6 X 50 MM |
6 MM |
7/16? |
BOX |
100 |
8 X 100 |
M8 X 55 MM |
8 MM |
1/2? |
BOX |
50 |
8 X 50 |
M8 X 75 MM |
8 MM |
1/2? |
BOX |
50 |
8 X 50 |
M10 X 65 MM |
10 MM |
9/16? |
BOX |
50 |
8 X 50 |
M10 X 75 MM |
10 MM |
9/16? |
BOX |
50 |
8 X 50 |
M10 X 100 MM |
10 MM |
9/16? |
BOX |
50 |
8 X 50 |
M10 X 150 MM |
10 MM |
9/16? |
BOX |
30 |
8 X 30 |
M12 X 75 MM |
12 MM |
3/4? |
BOX |
40 |
8 X 40 |
M12 X 100 MM |
12 MM |
3/4? |
BOX |
25 |
8 X 25 |
M12 X 150 MM |
12 MM |
3/4? |
BOX |
20 |
8 X 20 |
M16 X 100 MM |
16 MM |
15/16? |
BOX |
20 |
8 X 20 |
M16 X 150 MM |
16 MM |
15/16? |
BOX |
10 |
8 X 10 |
HARDBOLT ANCHOR BOLT – STAINLESS STEEL
DESCRIPTION |
RECOMMENDED
DRILL BIT |
TIGHTENING
WRENCH |
U.M. |
QUANTITY PER PACKAGE – PORTIONED (PIECE) |
QUANTITY PER PACKAGE – MASTER (PIECE) |
M8 X 75 MM |
8 OR 9 MM |
1/2? |
BOX |
50 |
7 X 50 |
M8 X 100 MM |
8 OR 9 MM |
1/2? |
BOX |
50 |
7 X 50 |
COMPOSITION
HARDBOLT ANCHOR BOLT – CARBON STEEL:
Material: Carbon steel with thermal treatment
FINISHING |
LAYER THICKNESS |
RESISTANCE TO CORROSION |
SALT-SPRAY¹ |
KESTERNICH² |
ECOSEAL 10K |
15 MICRONS |
240 HOURS |
10 CYCLES |
WHITE GALVANIZED |
5 MICRONS |
48 HOURS |
N/A³ |
GALVANIZED |
5 MICRONS |
48 HOURS |
N/A³ |
1 – Standards ASTM B117, ABNT NBR 8094 and DIN 50021 (red corrosion)
2 – Standard DIN 50018 (allowing 15% of red corrosion in the bolt head)
3 – Non-applicable
HARDBOLT ANCHOR BOLT – STAINLESS STEEL:
Material: Stainless steel SS 316 body and carbon steel tip
FINISHING |
LAYER THICKNESS |
RESISTANCE TO CORROSION |
|
SALT-SPRAY¹ |
KESTERNICH² |
ECOSEAL³ |
N/A4 |
N/A4 |
N/A4 |
1 – Standards ASTM B117, ABNT NBR 8094 and DIN 50021 (red corrosion)
2 – Standard DIN 50018 (allowing 15% of red corrosion in the bolt head)
3 – The Ecoseal coating in the Stainless Steel Hardbolt anchor bolts as a protection function against the galvanic cell and lubricity at the installation time
4 – Stainless steels have high Resistance to corrosion, and the tests 1 and 2 are not applicable
BREAKDOWN LOADS – FCK CONCRETE = 20 MPA
HARDBOLT ANCHOR BOLT – CARBON STEEL:
DIAMETER |
M6 |
M8 |
M10 |
M12 |
M16 |
FILLING (MM) |
45 |
50 |
70 |
60 |
70 |
100 |
70 |
100 |
125 |
95 |
125 |
TRACTION (KGF) |
710 |
1440 |
2570 |
2145 |
2755 |
4360 |
3190 |
4425 |
6640 |
4620 |
6980 |
SHEARING (KGF) |
915 |
1270 |
1470 |
1530 |
1735 |
2510 |
2895 |
4065 |
5080 |
4445 |
5475 |
HARDBOLT ANCHOR BOLT – STAINLESS STEEL:
DIAMETER |
M8 X 75 |
M8 X 100 |
FILLING (MM) |
40 |
60 |
70 |
50 |
70 |
DRILL BIT |
8 mm |
9 mm |
8 mm |
9 mm |
8 mm |
9 mm |
8 mm |
9 mm |
8 mm |
9 mm |
TRACTION (KGF) |
590 |
470 |
100 |
710 |
1280 |
830 |
740 |
590 |
1280 |
830 |
SHEARING (KGF) |
600 |
600 |
730 |
730 |
800 |
800 |
660 |
660 |
800 |
800 |
ALLOWED BREAKDOWN – FCK CONCRETE = 20 MPA
HARDBOLT ANCHOR BOLT – CARBON STEEL:
DIAMETER |
M6 |
M8 |
M10 |
M12 |
M16 |
FILLING (MM) |
45 |
50 |
70 |
60 |
70 |
100 |
70 |
100 |
125 |
95 |
125 |
TRACTION (KGF) |
180 |
360 |
645 |
535 |
690 |
1090 |
800 |
1105 |
1660 |
1155 |
1745 |
SHEARING (KGF) |
230 |
320 |
370 |
385 |
435 |
630 |
725 |
1015 |
1270 |
1110 |
1370 |
HARDBOLT ANCHOR BOLT – STAINLESS STEEL:
DIAMETER |
M8 X 75 |
M8 X 100 |
FILLING (MM) |
40 |
60 |
70 |
50 |
70 |
DRILL BIT |
8 mm |
9 mm |
8 mm |
9 mm |
8 mm |
9 mm |
8 mm |
9 mm |
8 mm |
9 mm |
TRACTION (KGF) |
145 |
120 |
250 |
180 |
320 |
210 |
185 |
145 |
320 |
210 |
SHEARING (KGF) |
150 |
150 |
180 |
180 |
200 |
200 |
165 |
165 |
200 |
200 |
Safety coefficient applied: 4.0. The values of the table refer to situations with a single anchor bolt and meet the minimum conditions for the edge.
ANCHOR BOLT DRAWING: